Comparison of dyeing of polyester fibers with natural dye and bio-mordant
نویسندگان
1 Department of Chemical Engineering, Jadavpur University, 188, Raja S. C. Mallick Road, Kolkata- 700032, India.
2 Department of Chemical Engineering, Jadavpur University, 188, Raja S. C. Mallick Road, Kolkata- 700032, India.
3 Department of Chemical Engineering, Jadavpur University, 188, Raja S. C. Mallick Road, Kolkata- 700032, India.
doi
10.30509/pccc.2018.76663چکیده
In this study, dyeing of two regenerated polyester fibers, poly-trimethylene terephthalate (PTT) and poly-lactic acid (PLA), with natural dyes were compared with that of poly-ethylene terephthalate (PET) fiber. Lac was used as the primary natural colorant while Catechu was chosen as a natural color that can also act as a biomordant. The effects of temperature, initial pH of dye bath and dyeing time on color strength of the fibers were examined with Lac and Lac-Catechu combination. The results indicated the regenerated polyester fibers to have more number of functional groups and less compact structure than PET, favoring dyeing under milder conditions. PTT exhibited higher color uptake than the other fibers. Also, with Lac and Catechu in the same dye bath, the color strength was found to increase for all fibers, indicating that Catechu acted as a biomordant. Response Surface Methodology (RSM) based on 23-Central Composite Design (CCD) was used for optimization of dyeing of PTT with Lac-Catechu combination. The optimal values for temperature, initial pH and dyeing time were found to be 127OC, 6 and 26 min, respectively. The quadratic regression model developed was found to be statistically significant using ANOVA, with R2-value and adjusted R2-value of 0.9708 and 0.9271 respectively.