Fabrication and Investigation of Se-Ge Glass-Ceramics in the Presence of Ga and Sn Additives
نویسندگان
1 Department of Material Engineering, University of Tabriz, Tabriz, Iran
2 Department of Material Engineering, Isfahan University of Technology, Isfahan, Iran
3 Department of Material Engineering, Isfahan University of Technology, Isfahan, Iran
4 Department of Material Engineering, University of Tabriz , Tabriz, Iran.
5 Department of Material Engineering, University of Tabriz, Tabriz, Iran
doi
10.30501/acp.2019.100461چکیده
The Chalcogenide glasses were fabricated by melting and quenching techniques in the Se-Ge system at the presence of 1mol% Ga and 3, 5, and 7mol% Sn. Differential Scanning Calorimetry (DSC) analysis was conducted to extract the heat treatment of the samples. Fourier Transform Infrared (FTIR) spectroscopy analysis was also performed in a range of 2-16µm. The Glass samples were heat-treated at 450°C for 1-10h. The precipitated nanoparticles were observed using a Field Emission Scanning Electron Microscope (FESEM). The crystal size was reported in the range of 100-1000nm. The precipitated phases were identified using X-ray Diffraction (XRD) analysis on Glass-Ceramics powder. The increase in hardness of the Glass-Ceramics was reported in the range of 200-250Kg.mm-2.