The Comparison of MgO and TiO2 Additives Role on Sintering Behavior and Microstructures of Reaction-Sintered Alumina-Zirconia-Mullite Composite
نویسندگان
1 Department of Ceramic, Islamic Azad University, Tehran
2 Faculty of Engineering and Technology, Imam Khomeini International University (IKIU)
3 School of Metallurgy and Material Engineering, Iran University of Science and Technology (IUST)
doi
10.30501/acp.2015.90744چکیده
Alumina-Mullite-Zirconia ceramic composites were prepared by reaction sintering of alumina, zircon mixture and the sintering aids of magnesia and titania at temperatures of 1400 and 1600 C for 2 hours. The development of different phases and microstructures of the composites were analysed to assess the relative influence of the additives on the formation of alumina-zirconia-mullite composite. Bulk density, phase combination, and microstructure of the sintered samples were examined by Archimedes method, X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. The results of the study revealed the successful formation of the alumina-mullite-zirconia composite by the reaction sintering method at temperature of 1600C. By the same token, the sample containing 6 wt.% of sintering aid shows improvement in density.