In this work, a 1:1 molar ratio of TiO2 and barium salts was used to prepare a BaTiO3 nanocomposite. A precursor solution was prepared through the chemical precipitation method and then hydrothermally treated to achieve different morphologies and structural forms of the nanocomposite. X-ray diffraction, which was used for structural characterization, demonstrated that the nanocomposite had an average particle size of approximately 56 nm and validated its crystalline nature. Surface morphology and particle size were assessed through scanning electron microscopy. The elemental composition and weight percentages of constituent elements were also determined by employing energy-dispersive X-ray spectroscopy to confirm the effective synthesis of the nanocomposite. These results were then compared with the anticipated theoretical values.