Amalgam Surface Treatment by Different Output Powers of Er:YAG Laser:SEM Evaluation
نویسندگان
1 Department of Orthodontics, School of Dentistry, Qom University of Medical Sciences, Qom, Iran
2 Laser Research Center of Dentistry, Dental Research Institute, Tehran University of Medical Sciences, Tehran, Iran
3 Department of restorative, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran
4 Laser Research Center of Dentistry, Dental Research Institute, Tehran University of Medical Sciences, Tehran, Iran.
5 Department of Orthodontics, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran
6 Department of Orthodontics, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran
doi
5865چکیده
Introduction: The purpose of this study was to evaluate amalgam surfaces treated by different output powers of erbium-doped yttrium aluminum garnet (Er:YAG) laser by scanning electron microscope (SEM).Methods: Twenty-one amalgam blocks (8 mm × 8 mm, 3 mm thickness) were prepared by condensing silver amalgam (into putty impression material. After keeping them for 24 hours in distilled water, they were divided into 7 groups as follow: G1: Er:YAG laser (1 W, 50 mJ), G2: Er:YAG laser (2 W, 100 mJ), G3: Er:YAG laser (3 W, 150 mJ), G4: Sandblast, G5: Sandblast + Er:YAG laser (1 W, 50 mJ), G6: Sandblast +Er:YAG laser (2 W, 100 mJ) and G7: Sandblast +Er:YAG laser (3 W, 150 mJ). Then after preparation of all samples, they were examined by SEM.Results: The SEM results of amalgam surfaces treated by different output powers of Er:YAG laser showed some pitting areas with non-homogenous irregularitiesConclusion: It seems that the application of sandblasting accompanied by Er:YAG laser irradiation can provide proper surface for bonding of orthodontic brackets.